Effect of nanostructured grains in co-sputtered Ni-GDC thin-film anode on methane conversion kinetics for low temperature solid oxide fuel cells operating on nearly dry methane

Direct-methane solid oxide fuel cells (DMSOFCs) have recently attracted substantial attention due to their simplified system, reduced cost, and the direct availability of methane fuel obtained from natural gas. Among oxygen-ion conductive materials, doped-ceria such as gadolinium-doped ceria (GDC) or samarium-doped ceria can be incorporated into Ni-based anodes to reinforce their coking resistance, enlarge their electrochemical reaction area, and improve the kinetics of the internal reforming/electrochemical oxidation of methane. To reduce the range of operating temperatures of DMSOFCs while maintaining their performance, the thin film deposition technique of magnetron sputtering was adopted in this work. An Ni-GDC thin-film anode and a Pt thin-film cathode were deposited on scandia-stabilized zirconia (ScSZ) electrolyte supports. This fuel cell was tested with directly supplied methane fuel (3% H₂O) at 500 °C. The results demonstrated the effects of the GDC volume fraction in the anode—which was controlled by co-sputtering power—on open circuit voltage and electrochemical performance. The co-sputtered Ni-GDC anode was able to survive through 36-h operation, although there was some performance degradation. Field-emission scanning electron microscopy results revealed no formation of filamentous carbon on the Ni catalysts, despite the fact that both X-ray photoelectron spectroscopy and Raman spectroscopy analyses detected carbon coking. The relatively high performance and resistance to carbon coking of co-sputtered thin-film anode were attributed to its intrinsic small grain size.     

Physical and electrochemical behavior of affordable Na3SbS4 solid electrolyte at different heat treatment temperatures

High-capacity and affordable all-solid-state Na-ion batteries have gathered increasing interest in recent years owing to low-cost sodium, which contributes to reducing the price of these Na-ion batteries to approximately 70% of that in lithium batteries. However, in terms of electrolyte performance and battery cost, the complete replacement of lithium batteries has a long way to go. In this work, low-cost and high-safety Na₂S·9H₂O materials are used in synthesizing Na₃SbS₄ solid electrolyte, the price of which is only one-fifth that of high-purity Na₂S. The structure and electrochemical properties are studied through X-ray diffraction analysis, Raman spectroscopy, scanning electron microscopy, and electrochemical tests. Results indicate that a multiphase Na₃SbS₄ structure containing cubic and tetragonal phases formed after heat treatment at 300 °C. In addition, a third phase transition of Na₃SbS₄ is inferred after further heating at 600 °C. This phase structure contributes to the improvement of electrochemical performance by promoting increasing ionic conductivity to 0.54 mS cm^?1 at room temperature (25 °C) and reducing activation energy to 0.076 eV. This work provides an affordable material with good electrochemical properties and not only simplifies the preparation but also greatly reduces the risk of the process.     

Optimizing the stability and electrical transport properties of CeNbO4+δ-based oxide ceramics by regulating oxygen ion content

CeNbO_4+δ ceramics have attracted extensive research interest because of their unique mixed ion-electron transport characteristics and interesting structure-functional characteristics caused by the difference in oxygen ion content. Although the change of oxygen ion content brings rich redox properties, it also causes serious crystal transformation and abnormal electrical transport properties. In order to obtain stable structure and excellent electrical transport properties, the directional regulation of the oxygen ion content has been realized through introducing Al₂O₃ and high temperature aging. After 600 h of aging at 1073 K, the prepared composite ceramics not only obtain a stable structure without crystal transformation, but also show good negative temperature coefficient (NTC) thermistor characteristics in the temperature range of 473 K–1273 K, in which the linear fitting maximum Pearson's r of the relationship between lnρ and 1000/T can reach 99.97%. The proposed method provides a new thought for the design and application of high-temperature electronic ceramics.     

Zirconium-diboride silicon-carbide composites: A review

Zirconium diboride (ZrB₂) and silicon carbide (SiC) composites have long been of interest since it was observed that ZrB₂ improved the thermal shock resistance of SiC. However, processing of these materials can be difficult due to high and different sintering temperatures and differences in the thermodynamic stability of each material. ZrB₂–SiC composites have been processed in a variety of ways including hot-pressing, spark-plasma sintering, reactive melt infiltration, pack cementation, chemical vapor deposition, chemical vapor infiltration, stereolithography, direct ink writing, selective laser sintering, electron beam melting, and binder jet additive manufacturing. Each manufacturing method has its own pros and cons. This review serves to summarize more than 60 years of research and provide a coherent resource for the variety of methods and advancements in development of ZrB₂–SiC composites.     

Influence of substrate temperature on the microstructure of YSZ films and their application as the insulating layer of thin film sensors for harsh temperature environments

Thin film sensors are employed to monitor the health of hot-section components of aeroengine intelligence (for instance, blades), and electrical insulating layers are needed between the metal components and thin film sensors. For this purpose, the electrical insulation characteristics of an yttria-stabilized zirconia (YSZ)/Al₂O₃ multilayer insulating structure were investigated. First, YSZ thin films were deposited by DC reactive sputtering at various substrate temperatures, and the microstructural features were investigated by scanning electron microscopy and X-ray diffraction. The results indicate that the micromorphology of the YSZ thin film gradually became denser with increasing substrate temperature, and no new phases appeared. The compact and uniform topography of the YSZ thin film improved the insulation properties of the multilayer insulating structure and enhanced the adhesion of the thin film sensors. In addition, the electrical insulation properties of the YSZ/Al₂O₃ multilayer insulating structure were evaluated via insulation resistance tests from 25 to 800 °C, in which the YSZ thin film was deposited at 550 °C. The results show that the insulation resistance of the multilayer structure increased by an order of magnitude compared with that of the conventional Al₂O₃ insulating layer, reaching 135 kΩ (5.1 × 10^?6 S/m) at 800 °C. Notably, the insulation resistance was still greater than 75 kΩ after annealing at 800 °C for 5 h. Finally, the shunt effect of the YSZ/Al₂O₃ multilayer insulating structure was estimated using a PdCr thin film strain gauge. The relative resistance error was 0.24%, which demonstrates that the YSZ/Al₂O₃ multilayer insulating structure is suitable for thin film sensors.     

Influence of the SiC matrix introduction time on the microstructure and mechanical properties of Cf/Hf0.5Zr0.5C-SiC ultra-high temperature composites

C_f/Hf_0.5Zr_0.5C-SiC composites were prepared by introducing Hf_0.5Zr_0.5C matrix (11 cycles) and SiC matrix (9 cycles) into the carbon cloth preform through precursor impregnation and pyrolysis (PIP) process. The influence of the introduction time of SiC matrix on the microstructure and mechanical properties of C_f/Hf_0.5Zr_0.5C-SiC composites was studied, and the results show that with the increase of the PIP cycles of the SiC matrix introduced before Hf_0.5Zr_0.5C matrix, the composite open porosity decreased, and the flexural strength and modulus presented an obvious upward trend. CS45 sample, which has 4 cycles of PIP SiC introduced in advance, has the highest flexural strength, flexural modulus and interfacial shear strength of 402.73 ± 35.73 MPa, 56.92 ± 3.97 GPa and 100.88 ± 7.79 MPa, respectively. Hf_0.5Zr_0.5C matrix has a loose and porous structure, so when more SiC matrix was introduced in advance, its covering effect on the surface of fibers led to less intra-bundle pores and thusly denser composite structure, and due to the compactness of SiC matrix, better overall bonding of fiber, interface and matrix was achieved, as well as better load transfer effect, which led to obvious interfacial debonding and cracking based on the in-situ SEM observation during flexural tests. While in the sample without pre-introduced SiC, the cracking occurred mainly between the interface and porous matrix and the overall performance of the material was poor.     

低共熔溶剂用于CO2捕集的研究进展

低共熔溶剂(DESs)具有原料廉价易得、化学稳定性好、可设计、合成工艺简单、可循环使用和绿色环保等优点,在CO₂捕集领域受到广泛关注。重点综述了近年来DESs用于CO₂捕集的研究进展,总结了DESs捕集CO₂的能力,分析了DESs捕集CO₂的影响因素和DESs的循环使用性能,归纳了DESs捕集CO₂的机理(包括物理吸收、化学吸收和物理化学协同吸收),并总结了CO₂在DESs中的溶解度计算模型。分析发现,DESs捕集CO₂的影响因素中,温度、压力和水含量(质量分数)均对CO₂的捕集有影响,且DESs的结构是重要的影响因素;大部分DESs可循环使用;CO₂在DESs中溶解度计算模型的建立有效推动了DESs捕集CO₂的进一步发展。最后,指出了DESs捕集分离CO₂所面临的主要问题并对进一步的研究工作进行了分析讨论。     

Effects of particle size distribution and sintering temperature on properties of alumina mold material prepared by stereolithography

Alumina mold materials prepared by stereolithography usually have considerable sintering shrinkage, and their properties related to casting have been rarely studied. In this study, alumina molds materials were prepared by stereolithography, and the effects of particle size distribution and sintering temperature on the properties of the materials were investigated. Results show that the viscosity of the slurries decreases as the fraction of fine powder increases, and the particle size distribution affects the curing behaviors slightly. Sintering shrinkage increases as the fraction of fine powder or the sintering temperature increases. Although lower sintering shrinkage can be achieved by sintering at 1350 °C or 1450 °C, the mold materials sintered at lower temperatures would continue to shrink under the service temperature of 1550 °C, and thus 1550 °C is determined as the optimal sintering temperature. As the fraction of fine powder increases, the creep resistance first increases and then decreases, and specimens prepared with 0.1 fraction of fine powder exhibit the best creep resistance with the droop distance of 4.44 ± 0.45 mm. Specimens prepared with 0.1 fraction of fine powder and sintered at 1550 °C exhibit linear shrinkage of 6.36% along the X/Y direction and 11.39% along the Z direction, and have a flexural strength of 78.15 ± 3.50 MPa and porosity of 30.12 ± 0.08%. The resulting material possesses relatively low sintering shrinkage, proper mechanical strength, porosity and high-temperature properties that meet the requirements for casting purposes.     

Orthorhombic to tetragonal polymorphic transformation of YTa3O9 and its inhibition through the design of high-entropy (Y0.2La0.2Ce0.2Nd0.2Gd0.2)Ta3O9

To explore the mechanism of phase transformation, YTa₃O₉ was prepared by an integrated one-step synthesis and sintering method at 1500 °C using Y₂O₃ and Ta₂O₅ powders as starting materials. High-temperature XRD patterns and Raman spectra showed that a phase transformation from orthorhombic to tetragonal took place in YTa₃O₉ through the bond length and angle changes at 300–400 °C, which caused a thermal conductivity rise. To inhibit the phase transformation, a high-entropy (Y_0.2La_0.2Ce_0.2Nd_0.2Gd_0.2)Ta₃O₉ (HE RETa₃O₉) was designed and synthesized at 1550 °C using the integrated solid-state synthesis and sintering method. In tetragonal structured HE RETa₃O₉, phase transformation was inhibited by the high-entropy effect. Furthermore, HE RETa₃O₉ exhibited low thermal conductivity, and its tendency to increase with temperature was alleviated (1.69 W/m·K, 1073 K). Good phase stability, low thermal conductivity and comparable fracture toughness to YSZ make HE RETa₃O₉ promising as a new thermal barrier coating material.     

Effect of temperature on the structure and mechanical properties of SiC–TiB2 composite ceramics by solid-phase spark plasma sintering

SiC composite ceramics have good mechanical properties. In this study, the effect of temperature on the microstructure and mechanical properties of SiC–TiB₂ composite ceramics by solid-phase spark plasma sintering (SPS) was investigated. SiC–TiB₂ composite ceramics were prepared by SPS method with graphite powder as sintering additive and kept at 1700 °C, 1750 °C, 1800 °C and 50 MPa for 10min.The experimental results show that the proper TiB₂ addition can obviously increase the mechanical properties of SiC–TiB₂ composite ceramics. Higher sintering temperature results in the aggregation and growth of second-phase TiB₂ grains, which decreases the mechanical properties of SiC–TiB₂ composite ceramics. Good mechanical properties were obtained at 1750 °C, with a density of 97.3%, Vickers hardness of 26.68 GPa, bending strength of 380 MPa and fracture toughness of 5.16 MPa m^1/2.